Heat Distortion and Vicat Softening Point Temperature Tester，Complies with the requirements of standards such as GB/T8802-2001, 1SO2570 rigid polyethylene (PVC)ECT

It is mainly used for the determination of heat deformation and Vicat softening point temperature of polymer materials (such as plastics, rubber, nylon, electrical insulating materials, etc.). Complies with the requirements of standards such as GB/T8802-2001, 1SO2570 rigid polyethylene (PVC), GB/T 1633, GB/T1634, 1SO75-1987 (E), 1SO306-1987 (E), etc.
Main performance indicators
Test range: Room temperature to 300℃
Number of sample racks: 2, 3, 6;
Heater power: 4KW;
Maximum deformation: 1mm.
Deformation resolution: 0.005mm
Heating rate: A=5℃ /6min, B=12℃/6min;
Overall dimensions: 520×420×1100mm;
DX8544HR-150 Rockwell hardness tester
With the specified indenter, apply the initial test force first, then the main test force, and then return to the initial test force. Conduct two initial tests in sequence
The value obtained from the difference in the depth of the indenter's penetration under the force test. It complies with the standard GB9342 "Test Method for Rockwell Hardness of Plastics".
Measurement range: 20-88 Hra, 20-100HRB, 20-70HRC
Maximum specimen height: 200mm
Initial test force: 98.1N/10Kgf
Total test force: 588.4N/60Kgf, 980.7N/100Kgf, 1471N/150Kgf
Total test force holding time: 10 seconds
Hardness scales: A, B, C
Overall dimensions: 466mm×250mm×618
Net weight: 80kg